Research on the lack of alloying in the galvannealed coating of automotive sheet steel 被引量:1

Research on the lack of alloying in the galvannealed coating of automotive sheet steel
下载PDF
导出
摘要 Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction (XRD) tests were carried out. The study discovers that the deficit of alloying was higher on both sides of the steel sheet when compared to the center and the thickness of the coating on the sides was also higher than the center. The results of the XRD tests demonstrate that the microstructure of the coating with a lack of alloy is mainly composed of zinc,ζ and δ. They also indicate that the lack of alloying is mainly due to a lower galvannealing temperature and thicker coating. It is shown by the optical micrographs of coating that the δ phase forms first in a discontinuous manner at the interface and then rapidly pushes towards the coating and enlarges. Samples of the cross section microstructures of galvannealed steel sheets that lack alloying were analyzed. X-ray diffraction (XRD) tests were carried out. The study discovers that the deficit of alloying was higher on both sides of the steel sheet when compared to the center and the thickness of the coating on the sides was also higher than the center. The results of the XRD tests demonstrate that the microstructure of the coating with a lack of alloy is mainly composed of zinc,ζ and δ. They also indicate that the lack of alloying is mainly due to a lower galvannealing temperature and thicker coating. It is shown by the optical micrographs of coating that the δ phase forms first in a discontinuous manner at the interface and then rapidly pushes towards the coating and enlarges.
出处 《Baosteel Technical Research》 CAS 2008年第4期17-20,共4页 宝钢技术研究(英文版)
关键词 automotive steel sheet lack of alloying COATING galvannealed steel sheet CRACKING automotive steel sheet lack of alloying coating galvannealed steel sheet cracking
  • 相关文献

参考文献9

  • 1Burghardt A J C,,A van der Heiden,Schoen J P,et al. Proc.Of2nd Int. Conf. on zinc and zinc alloy coated sheet steel GALVATECH’92 . 1992
  • 2Ghoniem M A,Lohberg K.The effect of steel chemistry on the formation of galvanneal-coated sheet steel[].Metall.1972
  • 3Paik Doojin,Chin Kwanggeun,Hong Moonhi.Prediction model of the galvannealing states using galvanneal phases ratio by X-ray diffraction during galvannealing process [ C][].GALVATECH‘.2007
  • 4Taniyama A.Quantitative analysis of galvannealing reaction by means of in-situ observation with synchrotron radiation[].Bulletin of the Iron and Steel Institute of Japan.2005
  • 5Taniyama A,Arai M,Takayama T.Initial stage reaction of Fe-Al intermetallic compounds during galvannealing process[].Galvatech’Proceedings.2004
  • 6Paik D,Kim J,Jin Y.The effects of galvannealing parameters on the change of surface morphologies and alloy phases ratio of the galvanneal coating [ C][].AISTechProceedings.2005
  • 7Shi MS,Smith G M,Moore M,et al.Zinc basedsteel coating systems[].Metallurgy and Perform-ance:The TMS Annual Meeting.1990
  • 8Massalski T B,Murry J L,Bennett L H, et al.Binary Alloy Phase Diagrams[]..1986
  • 9Hong M H,Saka H.Transmission Electron Microscopy ofthe Iron-Zincδ1 Intermetallic Phase[].Scripta Materialia.1997

同被引文献2

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部