Nonvolatile two-color holographic recording gated by incoherent ultraviolet （UV） light centered at 365 nm is investigated in near-stoichiometric lithium niobate crystals. The influence of thermal treatment on the two-color recording is studied. The results show that thermal reduction tends to improve the two-color recording performance, whereas thermal oxidation degrades the two-color recording. With an incoherent 0.2-W/cm2 UV gating light and a 0.25-W/cm2 semiconductor recording laser at 780 nm, a two-color recording sensitivity of 4 × 10^-3 cm/J and a recording dynamic range characterized by M/# of 0.12 are achieved in a 2.2-mm thermally reduced near-stoichiometric lithium niobate crystal. We attribute the improvement to the prolonged lifetime of small polarons and the increased absorption at the gating wavelength due to thermal reduction.
Nonvolatile two-color holographic recording gated by incoherent ultraviolet （UV） light centered at 365 nm is investigated in near-stoichiometric lithium niobate crystals. The influence of thermal treatment on the two-color recording is studied. The results show that thermal reduction tends to improve the two-color recording performance, whereas thermal oxidation degrades the two-color recording. With an incoherent 0.2-W/cm2 UV gating light and a 0.25-W/cm2 semiconductor recording laser at 780 nm, a two-color recording sensitivity of 4 × 10^-3 cm/J and a recording dynamic range characterized by M/# of 0.12 are achieved in a 2.2-mm thermally reduced near-stoichiometric lithium niobate crystal. We attribute the improvement to the prolonged lifetime of small polarons and the increased absorption at the gating wavelength due to thermal reduction.
基金
supported by the National Natural Science Foundation of China(No.60678021)
the Program for New Century Excellent Talents in University(NCET-04-0234)
the Program for Changjiang Scholars and Innovative Research Team in University(IRT0149)
the Municipal International Cooperation Program of Tianjin(No.06YFGHHZ00500)
the National"973"Program of China(No.2007CB307002)
the Chinese National Key Basic Research Special Fund(No.2006CB921703)
the 111 Project
the Cultivation Fund of the Key Scientific
Technical Innovation Project,Ministry of Education of China(No.708022)