An experimental set-up was designed and constructed to investigate the water vapor permeation through membranes.The test section mainly consisted of an airflow channel,a membrane,and a water tank,which formed a sandwich structure.The channel had a 5 mm×50 mm cross-section and a 800mm length.Flowing in the channel was an air fluid with a low humidity.The membrane was sandwiched between the channel and water tank,forming an air gap with a higher humidity between the water and membrane.Moisture was transferred from the water to the air stream in the channel through the air gap and membrane.Tests were conducted on two membranes that included the PVDF(polyvinylidene fluoride)and PES(poly ether sulfone)membranes.The water vapor permeations through membranes were investigated.The membrane resistance was obtained by subtracting the convective moisture resistance in the channel and the moisture resistance caused by the air gap from the total moisture resistance.Through combination with the sorption curves of membranes,the diffusivities of moisture in membranes were estimated.The results showed that the diffusivities of the PVDF and PES membranes were in the order of 10-6 kg·m-1·s-1,and the former was about 4 times as great as the latter.
An experimental set-up was designed and constructed to investigate the water vapor permeation through membranes. The test section mainly consisted of an airflow channel, a membrane, and a water tank, which formed a sandwich structure. The channel had a 5 mm× 50 mm cross-section and a 800mm length. Flowing in the channel was an air fluid with a low humidity. The membrane was sandwiched between the channel and water tank, forming an air gap with a higher humidity between the water and membrane. Moisture was transferred from the water to the air stream in the channel through the air gap and membrane. Tests were conducted on two membranes that included the PVDF （polyvinylidene fluoride） and PES （poly ether sulfone） membranes. The water vapor permeations through membranes were investigated. The membrane resistance was obtained by subtracting the convective moisture resistance in the channel and the moisture resistance caused by the air gap from the total moisture resistance. Through combination with the sorption curves of membranes, the diffusivities of moisture in membranes were estimated. The results showed that the diffusivities of the PVDF and PES membranes were in the order of 10^-6kg·m^-1 . s^-1, and the former was about 4 times as great as the latter.
出处
《化工学报》
EI
CAS
CSCD
北大核心
2009年第1期28-34,共7页
CIESC Journal
基金
国家自然科学基金项目(50576040)~~
关键词
薄膜
水蒸气
传质阻力
吸附曲线
扩散系数
membrane
water vapor
mass transfer resistance
sorption curves
diffusivity