采用常压低温氩等离子体对珍珠纤维混纺纱进行改性处理。探讨了处理时间和处理功率对纱线的失重、强力和吸湿性能的影响,实验发现纱线失重随处理时间和功率的增大而持续增大,强力先增大后降低,吸湿性能得到明显提高。
The surface of peal fiber blended yarns was modified using normal atmosphere and low pressure argon plasma. The influence of the processing time and power to the yarn' weight loss, strength and hygroscopicity was discussed. It was found that the yarns' weight loss increased with the increace of the processing time and power, the strength lowered after the first increace and the hygroscopicity could be markedly improved.
出处
《纺织科技进展》
CAS
2009年第1期65-67,共3页
Progress in Textile Science & Technology
关键词
珍珠纤维
氩等离子体
失重
强力
吸湿性
pearl fiber
argon plasma
weight loss
strength
hygroscopicity