现浇板裂缝产生原因及预防

Crack-in-situ Causes and Prevention
下载PDF
导出
摘要 随着现浇砼板在建筑工程中的普及,使建筑工程的整体稳定性大大的得到了加强,结构的抗震性能也得到了很大的改善。但在使用过程中由于现浇板产生的裂缝也在一定程度上给使用带来了好多不便,并由此引发了很多矛盾纠纷。因此如何减少和避免裂缝的发生,就需要设计和施工都从各个不同方面来采取措施。尤其是施工过程的控制,无疑是控制裂缝发生的最有效的措施。 As the cast-in-place concrete panels in the popularity of the construction , the construction of the overall stability has been strengthened significantly and the seismic performance of the structure has been greatly improved. But, in the using course of cast-in-place, the cracks have brought a lot of inconvenience to a certain extent, and lead to many contradictions and disputes. To reduce and avoid the occurrence of cracks, it needed to take measures from different areas of designing and constructing, in particular, the control of the construction process was undoubtedly the effective measures which controlled the occurrence of cracks.
作者 唐旭
出处 《甘肃冶金》 2009年第1期99-100,共2页 Gansu Metallurgy
关键词 现浇板 裂缝 产生原因 预防 cast-in-place plate crack causes prevention
  • 相关文献

参考文献3

二级参考文献3

  • 1日本混凝土工程协会 周国均 等.混凝土裂缝调查及加强加固技术柜橱[M].,1992..
  • 2张冬梅 周文 等.混凝土裂缝自动压力灌浆技术的研究与应用.建筑物鉴定与加固论文集[M].,1995,10..
  • 3张雄,习志臻,王胜先,姚武.仿生自愈合混凝土的研究进展[J].混凝土,2001(3):10-13. 被引量:53

共引文献544

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部