YAl3 （BO3）4： Eu^3＋ phosphors were prepared by the conventional solid state reaction. The phase structure and morphology were investigated by X-ray diffraction （XRD） and scanning electron microscope （SEM）. Doping YAl3（BO3）4： Eu^3＋ phosphors with concentration of Eu^3＋ ions of 0, 2, 5, 8 and 10 mol% were studied and their luminescent properties at room temperature were discussed. The excitation spectrum of Y0.95Eu0.05Al3（BO3）4 was composed of a broad band centered at about 252 nm and a group of lines in the longer wavelength region. In the emission spectra, the peak wavelength was about 614 nm under a 252 nm UV excitation. The optimal doping concentration of Eu^3＋ ions in YAl3（BO3）4： Eu^3＋ phosphors was 8 mol%.
YAl3 （BO3）4： Eu^3＋ phosphors were prepared by the conventional solid state reaction. The phase structure and morphology were investigated by X-ray diffraction （XRD） and scanning electron microscope （SEM）. Doping YAl3（BO3）4： Eu^3＋ phosphors with concentration of Eu^3＋ ions of 0, 2, 5, 8 and 10 mol% were studied and their luminescent properties at room temperature were discussed. The excitation spectrum of Y0.95Eu0.05Al3（BO3）4 was composed of a broad band centered at about 252 nm and a group of lines in the longer wavelength region. In the emission spectra, the peak wavelength was about 614 nm under a 252 nm UV excitation. The optimal doping concentration of Eu^3＋ ions in YAl3（BO3）4： Eu^3＋ phosphors was 8 mol%.