Segregation of Niobium During Electroslag Remelting Process 被引量:8

Segregation of Niobium During Electroslag Remelting Process
原文传递
导出
摘要 Experiment was carried out after the process parameters were calculated by the model previously established. The relationship between interdendritic spacing and local solidification time (LST) mainly determined by process parameters was exposed. Furthermore, the extent of segregation was studied. The results indicate that LST and interdendritic spacing are the largest and the amount of Laves phase as a result of the niobium segregation is the highest in the center of the ingot, whereas the opposite results are obtained at the edge of ingot. The extent of element segregation and the amount of Laves phase can be reduced when appropriate parameters are used. Therefore, the duration of subsequent homogenization treatments for 718 is shortened and the alloy quality is improved. Experiment was carried out after the process parameters were calculated by the model previously established. The relationship between interdendritic spacing and local solidification time (LST) mainly determined by process parameters was exposed. Furthermore, the extent of segregation was studied. The results indicate that LST and interdendritic spacing are the largest and the amount of Laves phase as a result of the niobium segregation is the highest in the center of the ingot, whereas the opposite results are obtained at the edge of ingot. The extent of element segregation and the amount of Laves phase can be reduced when appropriate parameters are used. Therefore, the duration of subsequent homogenization treatments for 718 is shortened and the alloy quality is improved.
出处 《Journal of Iron and Steel Research(International)》 SCIE EI CAS CSCD 2009年第1期7-11,共5页 钢铁研究学报(英文版)
基金 Item Sponsored by Weaponry Pre-Research Fund (51412020304QT0901)
关键词 electroslag remelting Inconel 718 SEGREGATION local solidification time interdendritic spacing electroslag remelting Inconel 718 segregation local solidification time interdendritic spacing
  • 相关文献

参考文献2

二级参考文献10

共引文献35

同被引文献64

  • 1龙正东,马培立,仲增墉.IN706合金的热加工性能[J].钢铁研究学报,1996,8(2):31-34. 被引量:4
  • 2陈再枝,马党参.我国模具钢的发展战略分析[J].钢铁,2006,41(4):5-9. 被引量:17
  • 3张磊,尧军平,陈炳坤.电渣熔铸过程电流大小对金属熔池影响的数值模拟研究[J].铸造技术,2007,28(1):19-22. 被引量:10
  • 4郑磊,徐庭栋,邓群,司红,董建新.高温合金GH4169(Inconel 718)中磷晶界偏聚特性的实验研究[J].金属学报,2007,43(8):893-896. 被引量:12
  • 5MollJ H , Maniar G H, Muzyka D R. The microstructure of a new Fe - Ni - Base superalloy [ J ]. Metallurgical Transactions, 1971, 2 : 2141 -2151.
  • 6Schilke P W, Schwant R C. Alloy 706 use, process optimization, and future directions for GE gas turbine rotor materials [ C]//Superalloys 718, 625, 706 and Various Derivatives. USA: TMS, 2001 : 25 -34.
  • 7Schilke P W, Pepe J, Schwant P. C. Alloy 706 metallurgy and turbine wheel application superalloys [ C ] //Superalloys 718, 625, 706 and Various Derivatives. USA: TMS, 1994:1 -12.
  • 8Allen T, Burlet H, Nanstad R K, et al. Advanced structural [J]. MRS bulletin, 2009, 34-40.
  • 9Hoffelner W. Damage assessment in structural metallic materials for advanced nuclear plants [ J ]. Journal of materials science, 2010, 45(9): 2247 -2257.
  • 10Shibata T, Shudo Y, Yoshino Y. Effects of aluminum, titanium and niobium on the time -temperature -precipitation behavior [ C ] //SuperaUoys 718, 625, 706 and Various Derivatives. USA: TMS, 1996:153-162.

引证文献8

二级引证文献23

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部