Bi3.25La0.75 Ti3O12 （BLT） ferroelectric thin films are deposited by sol-gel method and annealed for crystallizaion in total l eccm N2/02 mixed gas with various ratio at 750℃ for 30rain. The effect of crystallization ambient on the structural and ferroelectric properties of the BLT films is studied. The growth direction and grain size of BLT film are revealed to affect ferroeleetric properties. Alter the BLT film is annealed in 20%O2, the largest P~ value is obtained, which is ascribed to an increase of random orientation and large grain size. The fatigue property is improved with the concentration of oxygen in the ambient increasing, which is ascribed to annealing in the ambient with high concentrated oxygen adequately decreasing the defects related to lack of oxygen.
Bi3.25La0.75 Ti3O12 （BLT） ferroelectric thin films are deposited by sol-gel method and annealed for crystallizaion in total l eccm N2/02 mixed gas with various ratio at 750℃ for 30rain. The effect of crystallization ambient on the structural and ferroelectric properties of the BLT films is studied. The growth direction and grain size of BLT film are revealed to affect ferroeleetric properties. Alter the BLT film is annealed in 20%O2, the largest P~ value is obtained, which is ascribed to an increase of random orientation and large grain size. The fatigue property is improved with the concentration of oxygen in the ambient increasing, which is ascribed to annealing in the ambient with high concentrated oxygen adequately decreasing the defects related to lack of oxygen.
基金
Supported by the Key Project of the National Nature Science Foundation of China under Grant Nos 90407023 and 60571009.