摘要
为了研究中间包保护渣中碳和V2O5含量对钢液氮含量的影响,选用CaO-SiO2-Al2O3系碱性渣作为基础渣系进行实验。通过对实验结果分析可知,渣中的碳和V2O5含量对钢液脱氮都有一定的影响,但效果不一样。
In order to research the influence of V2O5 and carbon content in the tundish powder onnitrogen content in liquid steel, the basic slag system of CaO-SiO2-Al2O3 was chosen as a basic ingredient in the experiment. The experiment results show that V2O5 and carbon contents in the tundish powder have some effects on removal of nitrogen from molten steel, but their results are different.
出处
《连铸》
2009年第2期9-11,共3页
Continuous Casting
关键词
钢液
氮含量
碳含量
V2O5含量
liquid steel
nitrogen content
carbon content
V2O5 content