Inorganic antibacterial materials consist of the antibacterial ions, the additives and the carrier. In this study, we synthesized a new inorganic antibacterialmaterial, of which Cu2+ and Ag+ were selected to be the bi-component antibacterial ions, cerous nitrate served as the additives, and the white carbon black was chosen as the carrier, which was prepared by a sol-gel method. The as-synthesized antibacterial material was characterized by inductively coupled plasma, particle size measurement instrument, scanning electron microscope and enumeration tests. The result showed that the amount of antibacterial ions and bacteriostasis rate of this new material are higher than those for the single-ion inorganic antibacterial material. In addition, the particle size of this material can be extended down to 7 μm with a narrow size distribution. Other advantages of this material are its loose and dispersive structure, good thermal and light stability. From the antibacterial experiment in rubber and the coating surface of metal, this new material showed promising results. The possible antibacterial mechanism was also proposed through all the experimental data in this study.
Inorganic antibacterial materials consist of the antibacterial ions, the additives and the carrier. In this study, we synthesized a new inorganic antibacterialmaterial, of which Cu2+ and Ag+ were selected to be the bi-component antibacterial ions, cerous nitrate served as the additives, and the white carbon black was chosen as the carrier, which was prepared by a sol-gel method. The as-synthesized antibacterial material was characterized by inductively coupled plasma, particle size measurement instrument, scanning electron microscope and enumeration tests. The result showed that the amount of antibacterial ions and bacteriostasis rate of this new material are higher than those for the single-ion inorganic antibacterial material. In addition, the particle size of this material can be extended down to 7 μm with a narrow size distribution. Other advantages of this material are its loose and dispersive structure, good thermal and light stability. From the antibacterial experiment in rubber and the coating surface of metal, this new material showed promising results. The possible antibacterial mechanism was also proposed through all the experimental data in this study.
基金
the National Nature Science Foundation of China (50574045)
the Specialized Research Fundfor the Doctoral Program of Higher Education (20050674003)
the Science Research Fund of Yunnan Provincial Department of Education(07Y41398)