摘要
The synthesis, composition optimization, VUV Photoluminescence (PL) spectra, and optical properties, of (Y,Gd)(V,P)O4∶Eu3+ phosphors were investigated by synchrotron radiation. The VUV PLE spectra and the correlation among VUV PL intensity, λem, and Eu3+, Gd3+, and P-content were established. The PLE spectral studies showed that (Y,Gd)(V,P)O4∶Eu3+ exhibited significant absorption in the VUV range. The VUV PL intensity was found to enhance with PO43- and Gd3+-doping. Furthermore, the chromaticity characteristics of (Y,Gd)(V,P)O4∶Eu3+ were also found to be (0.6614, 0.3286) and compared against (Y, Gd)BO3∶Eu3+ as a reference. Based on the characterization results, we are currently improving and evaluating the potential application of (Y,Gd)(V,P)O4∶Eu3+ as a new red-emitting PDP phosphor.
The synthesis, composition optimization, VUV Photoluminescence (PL) spectra, and optical properties, of (Y,Gd)(V,P)O4∶Eu3+ phosphors were investigated by synchrotron radiation. The VUV PLE spectra and the correlation among VUV PL intensity, λem, and Eu3+, Gd3+, and P-content were established. The PLE spectral studies showed that (Y,Gd)(V,P)O4∶Eu3+ exhibited significant absorption in the VUV range. The VUV PL intensity was found to enhance with PO43- and Gd3+-doping. Furthermore, the chromaticity characteristics of (Y,Gd)(V,P)O4∶Eu3+ were also found to be (0.6614, 0.3286) and compared against (Y, Gd)BO3∶Eu3+ as a reference. Based on the characterization results, we are currently improving and evaluating the potential application of (Y,Gd)(V,P)O4∶Eu3+ as a new red-emitting PDP phosphor.
基金
the National Science Council of Taiwan (NSC95 -2113-M-009-024-MY3)