Organic-dispersible lanthanide fluorides nanocrystals were synthesized at a large scale using colloid-extraction method, in the presence of dialkyl-dithiophosphinic acid (DDPA) as the extraction agent. The products were characterized by means of X-ray powder diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Fourier transformation infrared (FTIR) spectroscopy. It was found that the synthesized lanthanide fluorides nanoparticles had high purity and crystallinity, and could be well dispersed in organic solvents such as chloroform, toluene etc., which could be closely related to the surface-capping of the nanocrystals by the DDPA molecules. Moreover, the nanocrystals before and after extraction by DDPA showed few differences in the microscopic morphologies. It was implied that DDPA as the extraction agent had good protection to the nanocrystals as well, which could be essential to the commercial application of the titled rare earth nanocrystals as novel multifunctional additives in the fields of lubrication.
Organic-dispersible lanthanide fluorides nanocrystals were synthesized at a large scale using colloid-extraction method, in the presence of dialkyl-dithiophosphinic acid (DDPA) as the extraction agent. The products were characterized by means of X-ray powder diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), and Fourier transformation infrared (FTIR) spectroscopy. It was found that the synthesized lanthanide fluorides nanoparticles had high purity and crystallinity, and could be well dispersed in organic solvents such as chloroform, toluene etc., which could be closely related to the surface-capping of the nanocrystals by the DDPA molecules. Moreover, the nanocrystals before and after extraction by DDPA showed few differences in the microscopic morphologies. It was implied that DDPA as the extraction agent had good protection to the nanocrystals as well, which could be essential to the commercial application of the titled rare earth nanocrystals as novel multifunctional additives in the fields of lubrication.
基金
Project supported bythe National Natural Science Foundation of China (20401006)
Natural Science Foundation of Henan Province (200510475019)