摘要
The billets of a new super-high strength Al-Zn-Mg-Cu alloy in 200mm diameter were produced by the processesof low frequency electromagnetic casting (LFEC) and conventional direct chill (DC) casting, respectively. The effects of lowfrequency electromagnetic field on temperature field of the melt in the hot-top were investigated by temperaturemeasurement method. Temperature curves were measured from the surface to the center of the billets by locating type Kthermocouples into the casting during the processes. The results show that during LFEC process the temperature field inthe melt applying the hot-top is very uniform, which is helpful to reduce the difference of thermal gradients between thesurface and the center, and then to reduce the thermal stress and to eliminate casting crack.
The billets of a new super-high strength Al-Zn-Mg-Cu alloy in 200mm diameter were produced by the processesof low frequency electromagnetic casting (LFEC) and conventional direct chill (DC) casting, respectively. The effects of lowfrequency electromagnetic field on temperature field of the melt in the hot-top were investigated by temperaturemeasurement method. Temperature curves were measured from the surface to the center of the billets by locating type Kthermocouples into the casting during the processes. The results show that during LFEC process the temperature field inthe melt applying the hot-top is very uniform, which is helpful to reduce the difference of thermal gradients between thesurface and the center, and then to reduce the thermal stress and to eliminate casting crack.