To save energy and raise molding and coremaking productivity, the synthetic procedure of novolaks for the shell process was investigated. The study indicated that it was difficult to obtain fast curing novolaks under strongly acidic conditions alone. A novel synthetic procedure was proposed for preparing novolaks in a two-step manner, a divalent metal salt catalyzed novolak preparation followed by a strong acid catalyzed novolak preparation. The optimum conditions for the two-step procedure were determined by orthogonal experiment design. The results showed that it was easy to prepare fast curing novolaks with cure time in the range of 20 s to 30 s and softening point in the range of 80℃ to 90℃ under complex catalysis conditions.
To save energy and raise molding and coremaking productivity, the synthetic procedure of novolaks for the shell process was investigated. The study indicated that it was difficult to obtain fast curing novolaks under strongly acidic conditions alone. A novel synthetic procedure was proposed for preparing novolaks in a two-step manner, a divalent metal salt catalyzed novolak preparation followed by a strong acid catalyzed novolak preparation. The optimum conditions for the two-step procedure were determined by orthogonal experiment design. The results showed that it was easy to prepare fast curing novolaks with cure time in the range of 20 s to 30 s and softening point in the range of 80℃ to 90℃ under complex catalysis conditions.