The glass-ceramic was prepared on the basis of materials of granulated slag containing high-calcium oxide and cullet. The content of granulated slag ranges from 50% - 60% wt in the glass compositions. The samples were analyzed by DTA , SEM and XRD. The results show that the main crystal phase of the glass- ceramic is β-CaSiO3 , Which is in scattering fiber or column form. The applying properties have also been measured.
The glass-ceramic was prepared on the basis of materials of granulated slag containing high-calcium oxide and cullet. The content of granulated slag ranges from 50% - 60% wt in the glass compositions. The samples were analyzed by DTA , SEM and XRD. The results show that the main crystal phase of the glass- ceramic is β-CaSiO3 , Which is in scattering fiber or column form. The applying properties have also been measured.