The structure and magnetic properties of the intermetallic compounds Y(Fe 1- x Co x ) 11.3 Nb 0.7 ( x =0, 0 05, 0 1, 0 2) were studied by X ray diffraction and magnetic property measurements. X ray diffraction patterns and thermomagnetic curves show that all compounds almost exhibit single phase. All Y(Fe 1- x Co x ) 11.3 Nb 0.7 compounds ( x =0, 0 05, 0 1, 0 2) crystallize in ThMn 12 type structure. Substitution of Co for Fe leads to a clear increasing of Curie temperature and a monotonic decreasing of lattice constants. At room temperature the composition dependence of saturation magnetization exhibits a maximum at about x =0 1～0 2. The magnetocrystalline anisotropy field at room temperature at first increases and then decreases with the increasing of Co content.
The structure and magnetic properties of the intermetallic compounds Y(Fe 1- x Co x ) 11.3 Nb 0.7 ( x =0, 0 05, 0 1, 0 2) were studied by X ray diffraction and magnetic property measurements. X ray diffraction patterns and thermomagnetic curves show that all compounds almost exhibit single phase. All Y(Fe 1- x Co x ) 11.3 Nb 0.7 compounds ( x =0, 0 05, 0 1, 0 2) crystallize in ThMn 12 type structure. Substitution of Co for Fe leads to a clear increasing of Curie temperature and a monotonic decreasing of lattice constants. At room temperature the composition dependence of saturation magnetization exhibits a maximum at about x =0 1～0 2. The magnetocrystalline anisotropy field at room temperature at first increases and then decreases with the increasing of Co content.
基金
ProjectsupportedbyNaturalScienceFoundationofJiangxiProvince (995 0 0 3 5 )