The dendrite segregation in cast H13 steel was weakened with RE modification treatment. Grain boundary carbide during quenching was also under control and impact toughness was improved greatly. By thermodynamic calculation, analysis of two-dimensional lattice misfitting and electron probe analysis, it is found that Ce2O3 may act as the heterogeneous nuclei of modified cast H13 steel.
The dendrite segregation in cast H13 steel was weakened with RE modification treatment. Grain boundary carbide during quenching was also under control and impact toughness was improved greatly. By thermodynamic calculation, analysis of two-dimensional lattice misfitting and electron probe analysis, it is found that Ce2O3 may act as the heterogeneous nuclei of modified cast H13 steel.