摘要
Two new ultrathin multiplayer films have been successfully prepared fi-om Keggin-type heteropoly acids H-4[SiW12O40] and H-3[PMo12O40] with polyelectrolytes PEI, PSS, and PAH, using the electrostatic layer-by-layer self-assembly, technique. The XR results reveal their film thickness at nanoscale (similar to 20 nm). According to the AFM images, it is believed that the surface roughness (rough degree of film surface) of the polyelectrolyte-polyoxometalate film greatly depends on the kind of polyoxometalates.
Two new ultrathin multiplayer films have been successfully prepared fi-om Keggin-type heteropoly acids H-4[SiW12O40] and H-3[PMo12O40] with polyelectrolytes PEI, PSS, and PAH, using the electrostatic layer-by-layer self-assembly, technique. The XR results reveal their film thickness at nanoscale (similar to 20 nm). According to the AFM images, it is believed that the surface roughness (rough degree of film surface) of the polyelectrolyte-polyoxometalate film greatly depends on the kind of polyoxometalates.
基金
This project was financially supported by the National Natural Science Foundation of China (Grant No. 29971006 ).