Poly(ethylene methyl phosphate)-poly(ethylene glycol)-poly(ethylene methyl phosphate) triblock copolymers carrying hydroxyl group at both chain ends were synthesized with sodium poly(ethylene glycol)ate as initiator. The effects of the factors such as solvent, amount of the initiator and reaction time were investigated. The copolymers were characterized by IR, H-1-NMR, H-1{P-31}-NMR, C-13-NMR, P-31{H-1}-NMR, and DSC. High molecular weight of the copolymer and high yield of the polymerization were achieved within 3 min at 25 degrees C. The polymerization process was studied by P-31{H-1}-NMR and transesterification was found during longer polymerization time.
Poly(ethylene methyl phosphate)-poly(ethylene glycol)-poly(ethylene methyl phosphate) triblock copolymers carrying hydroxyl group at both chain ends were synthesized with sodium poly(ethylene glycol)ate as initiator. The effects of the factors such as solvent, amount of the initiator and reaction time were investigated. The copolymers were characterized by IR, H-1-NMR, H-1{P-31}-NMR, C-13-NMR, P-31{H-1}-NMR, and DSC. High molecular weight of the copolymer and high yield of the polymerization were achieved within 3 min at 25 degrees C. The polymerization process was studied by P-31{H-1}-NMR and transesterification was found during longer polymerization time.
基金
Supported by the National Natural Science Foundation of China.