Vinyl ether (VE)-based amphiphilic block copolymers with D-glucose residues as hydrophilicpendants were synthesized by CH_3 CH(OiBu)Cl/ZnI_2-initiated sequential living cationic copolymerization of3-O-(vinyloxy)ethyl-1, 2:5, 6-di-O-isopropylidene-D-glucofuranose (IGVE) and isobutyl VE (IBVE ) andsubsequent deprotection. The precursor block copolymers had a narrow molecular weight distribution(M_w/M_n～1.1) and a controlled segmental composition. The solubility characteristics of the amphiphiliccopolymer depended strongly on composition. Their solvent-cast thin films were examined, under atransmission electron microscope, and could be seen to exhibit various microphase-separated surfacemorphologies such as spheres, cylinders, and lamellae, depending on composition. The amphiphiliccopolymers with the appropriate segmental composition were found to form a stable monolayer at the air-water interface, which was successfully transferred onto a substrate by the Langmuir-Blodgett (LB)technique. The layered strucfure of the built-up LB films was controlled by blending the homopolymer.
Vinyl ether (VE)-based amphiphilic block copolymers with D-glucose residues as hydrophilicpendants were synthesized by CH_3 CH(OiBu)Cl/ZnI_2-initiated sequential living cationic copolymerization of3-O-(vinyloxy)ethyl-1, 2:5, 6-di-O-isopropylidene-D-glucofuranose (IGVE) and isobutyl VE (IBVE ) andsubsequent deprotection. The precursor block copolymers had a narrow molecular weight distribution(M_w/M_n～1.1) and a controlled segmental composition. The solubility characteristics of the amphiphiliccopolymer depended strongly on composition. Their solvent-cast thin films were examined, under atransmission electron microscope, and could be seen to exhibit various microphase-separated surfacemorphologies such as spheres, cylinders, and lamellae, depending on composition. The amphiphiliccopolymers with the appropriate segmental composition were found to form a stable monolayer at the air-water interface, which was successfully transferred onto a substrate by the Langmuir-Blodgett (LB)technique. The layered strucfure of the built-up LB films was controlled by blending the homopolymer.