摘要
Heterojunctions between polyaniline (PANI) and n-type porous silicon (PS), Al/PS-PANI/Au cell, were fabricated, and the rectifying parameters of this heterojunction diode were measured as a function of the preparation conditions of PANI and PS, the electronic structure of PANI as well as cell structure. The rectifying parameters of Al/PS-PANI/Au cell were determined to be gamma = 1.8x10(1) similar to 1.0x10(5) for the rectifying ratio at 3V, n = 3 similar to 12 for the ideal factor, j(0) = 8.0x10(-5) similar to 5.6x10(-2) mA/cm(2) for the reversed saturated current density, and phi(0) = 0.67 similar to 0.83 V for the barrier height, respectively. The best rectifying heterojunction diode made between PANI and n-type PS with higher rectifying factor (gamma = 1.0x10(5) at 3V), output current (>1500 mA/cm(2) at 3V) and lower ideal factor (n = 3.3) was obtained by preventing the oxidation of PS before evaporating Al electrode.
Heterojunctions between polyaniline (PANI) and n-type porous silicon (PS), Al/PS-PANI/Au cell, were fabricated, and the rectifying parameters of this heterojunction diode were measured as a function of the preparation conditions of PANI and PS, the electronic structure of PANI as well as cell structure. The rectifying parameters of Al/PS-PANI/Au cell were determined to be gamma = 1.8x10(1) similar to 1.0x10(5) for the rectifying ratio at 3V, n = 3 similar to 12 for the ideal factor, j(0) = 8.0x10(-5) similar to 5.6x10(-2) mA/cm(2) for the reversed saturated current density, and phi(0) = 0.67 similar to 0.83 V for the barrier height, respectively. The best rectifying heterojunction diode made between PANI and n-type PS with higher rectifying factor (gamma = 1.0x10(5) at 3V), output current (>1500 mA/cm(2) at 3V) and lower ideal factor (n = 3.3) was obtained by preventing the oxidation of PS before evaporating Al electrode.
基金
The project was supported by the Foundation of Chinese Academy of Sciences.