摘要
Liquid crystalline multi-block copolymers poly[1,6-bis(4-oxybenzoyl-oxy)hexane terephthalate]-b-bisphenol A polycarbonate (PHTH-6-b-PC) with different segments of polycarbonate (PC) and thermotropic polyester PHTH-6 were synthesized in tetrachloroethane at 144 similar to 146 degrees C. The influence of segment length on the resulting phase structure and thermal behavior of block copolymers was also discussed. It is demonstrated by TEM and DMA that the resulting block copolymers show a considerable microphase separation. The degree of phase separation and the thermal behavior of the block copolymers are strongly dependent on the molecular weight of the segments incorporated.
Liquid crystalline multi-block copolymers poly[1,6-bis(4-oxybenzoyl-oxy)hexane terephthalate]-b-bisphenol A polycarbonate (PHTH-6-b-PC) with different segments of polycarbonate (PC) and thermotropic polyester PHTH-6 were synthesized in tetrachloroethane at 144 similar to 146 degrees C. The influence of segment length on the resulting phase structure and thermal behavior of block copolymers was also discussed. It is demonstrated by TEM and DMA that the resulting block copolymers show a considerable microphase separation. The degree of phase separation and the thermal behavior of the block copolymers are strongly dependent on the molecular weight of the segments incorporated.