摘要
Two kinds of heterojunction diodes of porous silicon (PS) with soluble polyaniline (PANI) were fabricated. One is a heterojunction diode of PS with water-soluble copolymer of polyaniline (PAOABSA), Al/PS-PAOABSA/Au cell as rectifying diode. Another is a heterojunction diode of PS with soluble polyaniline doped with DBSA, Al/PS-PANI (DBSA)/Au cell as light emitting diode (LED). The rectifying characteristics of the rectifying diodes were measured as a function of the degree of sulfonation and thickness of the copolymers, as well as oxidation of PS. The rectifying ratio of the heterojunction can reach 5.0x10(4) at +/-3 V bias. For the LED, the photoluminescence (PL) and electroluminescence (EL) spectra were measured and discussed.
Two kinds of heterojunction diodes of porous silicon (PS) with soluble polyaniline (PANI) were fabricated. One is a heterojunction diode of PS with water-soluble copolymer of polyaniline (PAOABSA), Al/PS-PAOABSA/Au cell as rectifying diode. Another is a heterojunction diode of PS with soluble polyaniline doped with DBSA, Al/PS-PANI (DBSA)/Au cell as light emitting diode (LED). The rectifying characteristics of the rectifying diodes were measured as a function of the degree of sulfonation and thickness of the copolymers, as well as oxidation of PS. The rectifying ratio of the heterojunction can reach 5.0x10(4) at +/-3 V bias. For the LED, the photoluminescence (PL) and electroluminescence (EL) spectra were measured and discussed.
基金
Foundation of The Chinese Academy of Sciences