Poly (ethyl acrylate-co-lithium methacrylate) (PEM) latex film was synthesized by emulsion-free polymerization. The electrochemical window of plasticized PEM latex film is exceeding 5.0 V. LiCoO2/Li battery with PEM latex film as electrolyte exhibits excellent reversibility and when the discharge current density is 0.3 mA/cm(2), the specific discharge capacity achieves 4.4 mAh/cm(2).
Poly (ethyl acrylate-co-lithium methacrylate) (PEM) latex film was synthesized by emulsion-free polymerization. The electrochemical window of plasticized PEM latex film is exceeding 5.0 V. LiCoO2/Li battery with PEM latex film as electrolyte exhibits excellent reversibility and when the discharge current density is 0.3 mA/cm(2), the specific discharge capacity achieves 4.4 mAh/cm(2).