摘要
The influences of Ca substitution for Ml and surface treatment on electrochemical performances of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 hydrogen storage alloy electrode were investigated. Ca substitution with x <0.2 for Ml could improve its discharge capacity, but Ca substitution with x >0.2 could decrease the capacity. It was also found that Ca substitution deteriorates the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode. In order to improve these properties of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 alloy electrode, the alloy was treated in 6 mol/L KOH+0.02 mol/L KBH 4 solution. The results showed that the surface treatment improves the electrochemical performances such as the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode. :The influences of Ca substitution for Ml and surface treatment on electrochemical performances of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 hydrogen storage alloy electrode were investigated. Ca substitution with x <0.2 for Ml could improve its discharge capacity, but Ca substitution with x >0.2 could decrease the capacity. It was also found that Ca substitution deteriorates the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode. In order to improve these properties of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 alloy electrode, the alloy was treated in 6 mol/L KOH+0.02 mol/L KBH 4 solution. The results showed that the surface treatment improves the electrochemical performances such as the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode.
The influences of Ca substitution for Ml and surface treatment on electrochemical performances of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 hydrogen storage alloy electrode were investigated. Ca substitution with x <0.2 for Ml could improve its discharge capacity, but Ca substitution with x >0.2 could decrease the capacity. It was also found that Ca substitution deteriorates the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode. In order to improve these properties of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 alloy electrode, the alloy was treated in 6 mol/L KOH+0.02 mol/L KBH 4 solution. The results showed that the surface treatment improves the electrochemical performances such as the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode. :The influences of Ca substitution for Ml and surface treatment on electrochemical performances of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 hydrogen storage alloy electrode were investigated. Ca substitution with x <0.2 for Ml could improve its discharge capacity, but Ca substitution with x >0.2 could decrease the capacity. It was also found that Ca substitution deteriorates the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode. In order to improve these properties of Ml 1.0- x Ca x Ni 4.0 Co 0.6 Al 0.4 alloy electrode, the alloy was treated in 6 mol/L KOH+0.02 mol/L KBH 4 solution. The results showed that the surface treatment improves the electrochemical performances such as the electrocatalytic activity, high rate dischargeability and cycling durability of the alloy electrode.
出处
《中国有色金属学会会刊：英文版》
CSCD
1999年第3期487-492,共6页
Transactions of Nonferrous Metals Society of China