摘要
The effects of FeS 2 on the discharge characteristics of Li B alloy/FeS 2 thermal battery had been studied. Results showed that 2.5%(mass fraction)Li 2O would be needed to rule out the voltage pulse in the first part of discharge curves for the FeS 2 powder of small particle size (<44 μm). After thermal decomposition, the FeS 2 had transformed to Fe (1- x ) S where x =0.024～0.066. The deficiency of the cathode FeS 2 would make discharge voltage decrease 0.4 V. In the discharge test at high temperature (600 ℃), the discharge voltage decreased fast with the acceleration of the thermal decomposition of FeS 2.
The effects of FeS 2 on the discharge characteristics of Li B alloy/FeS 2 thermal battery had been studied. Results showed that 2.5%(mass fraction)Li 2O would be needed to rule out the voltage pulse in the first part of discharge curves for the FeS 2 powder of small particle size (<44 μm). After thermal decomposition, the FeS 2 had transformed to Fe (1- x ) S where x =0.024～0.066. The deficiency of the cathode FeS 2 would make discharge voltage decrease 0.4 V. In the discharge test at high temperature (600 ℃), the discharge voltage decreased fast with the acceleration of the thermal decomposition of FeS 2.
出处
《中国有色金属学会会刊：英文版》
CSCD
1999年第3期530-534,共5页
Transactions of Nonferrous Metals Society of China