摘要
The fatigue crack initiation from notch root and the short-crack growth laws of two medium carbon alloying structural steels—35CrMo and 42CrMo are investigated under the different stress ratios R =0.1, 0.3) and three-point bending condition. The relationships between the maximum stress range at the notch root Δ σ max and the number of cycles before fatigue crack initiation N i are determined. The threshold stresses of fatigue crack initiation (Δ σ max ) th are got, and the smallcrack growth laws are obtained for these steels. An effective and convenient method is proposed for predicting the fatigue life of the notch specimens.
The fatigue crack initiation from notch root and the short-crack growth laws of two medium carbon alloying structural steels—35CrMo and 42CrMo are investigated under the different stress ratios R =0.1, 0.3) and three-point bending condition. The relationships between the maximum stress range at the notch root Δ σ max and the number of cycles before fatigue crack initiation N i are determined. The threshold stresses of fatigue crack initiation (Δ σ max ) th are got, and the smallcrack growth laws are obtained for these steels. An effective and convenient method is proposed for predicting the fatigue life of the notch specimens.