The reduction rate of Fe^tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder has been determined in an alumina crucible at 1 673-1 823 K. The effects of temperature, slag basicity and Fe_tO content on the reduction rate have also been discussed. Test results show that the reduction rate increases with the increase of temperature or Fe_tO concentration in slags, and the reduction rate has a parabolic relation with slag simple basicity or optical basicity. The maximum reduction rate is observed around CaO/SiO_2=1.5 of molten slags. The reaction order is 1.26 or 1.31, and the reduction activation energy is 126.8 or 129.7 kJ/mol respectively in regard to Fe_tO content or Fe_tO activity calculated by using regular solution model. The reduction rate of Fe_tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder is in the range of 0.15×10^-4-0.86×10^-4 molO/cm^2·s.
The reduction rate of Fe^tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder has been determined in an alumina crucible at 1 673-1 823 K. The effects of temperature, slag basicity and Fe_tO content on the reduction rate have also been discussed. Test results show that the reduction rate increases with the increase of temperature or Fe_tO concentration in slags, and the reduction rate has a parabolic relation with slag simple basicity or optical basicity. The maximum reduction rate is observed around CaO/SiO_2=1.5 of molten slags. The reaction order is 1.26 or 1.31, and the reduction activation energy is 126.8 or 129.7 kJ/mol respectively in regard to Fe_tO content or Fe_tO activity calculated by using regular solution model. The reduction rate of Fe_tO in CaOSiO_2Al_2O_3Fe_tO slags with graphite powder is in the range of 0.15×10^-4-0.86×10^-4 molO/cm^2·s.