DEVELOPMENTOFMoS2CONTAININGNiCrBASEDALLOYSANDTHEIRHIGHTEMPERATURETRIBOLOGICALPROPERTIES①XiongDangshengColegeofMechanicalEl...
B and MoS2containing NiCr based selflubricating materials were prepared by P/M hotpressing the mixture of alloyed NiCr powder, elemental Mo and B powders and MoS2 powder. The phase constituents were analysed using an Xray diffractometer, and the hardness was measured using a Brinell's machine. The friction coefficients and wear rates of the studied materials were determined by means of pinondisc tribometer. The results showed that the studied materials are mainly composed of Nibased solid solution, Cr3S4 and MoB; the wear debris are mainly composed of NiO, CrO, xNiO·MoO3·yH2O, Cr2O3 and nickelbased solid solution at 700 ℃; the NiCrMoB4MoS2 alloy has the best tribological properties, over a wide range of temperature from 20 ℃ to 700 ℃, its friction coefficient is 0.14~0.26 and its wear rate is 1.6×10-14~1.2×10-13m3/N·m.