Zinc powder electrodeposited from suspension bath has higher corrosion resistance than that from conventional bath. The results of X ray, SEM and EIS (Electrochem. Impedance Spectrum) indicated that the microstructures of zinc powder could be modified according to the kinds of suspension species. Suspension of TiO 2, SiO 2, In 2O 3, PbO 2 and SnO 2 could obviously improve the polarization resistance of zinc powder anodes in 5 mol/L KOH solution.
Zinc powder electrodeposited from suspension bath has higher corrosion resistance than that from conventional bath. The results of X ray, SEM and EIS (Electrochem. Impedance Spectrum) indicated that the microstructures of zinc powder could be modified according to the kinds of suspension species. Suspension of TiO 2, SiO 2, In 2O 3, PbO 2 and SnO 2 could obviously improve the polarization resistance of zinc powder anodes in 5 mol/L KOH solution.