d-Al-Dy system materials were prepared by the technique of powder sintering. Twolayers gradient function materials with compositions of (Gd_0.9Dy_0.1)_3Al_2 and Gd_3Al_2 respectively were studied. The results show that the Curie temperature (Tc) of the monolayer material decreases with the increment of Dy content. The Tc values of the twolayer gradient function material agree well with the layer numbers and corresponding to Dy content. For the Tc gradiently changed twolayers Gd-Al-Dy system material, its ΔSm changes smoothly with temperature. Therefore, the magnetic refrigeration is improved.
d-Al-Dy system materials were prepared by the technique of powder sintering. Twolayers gradient function materials with compositions of (Gd_0.9Dy_0.1)_3Al_2 and Gd_3Al_2 respectively were studied. The results show that the Curie temperature (Tc) of the monolayer material decreases with the increment of Dy content. The Tc values of the twolayer gradient function material agree well with the layer numbers and corresponding to Dy content. For the Tc gradiently changed twolayers Gd-Al-Dy system material, its ΔSm changes smoothly with temperature. Therefore, the magnetic refrigeration is improved.