摘要
At low concentrations of cetyltrimethylammonium bromide,all silica-based mesoporous materials with hexagonal phase have been synthesized via interactions between self-assembled surfactant molecule aggregates and aniomc silicate polymers.The resulting materials are characterized by XRD,FT-IR,solid state 29Si MAS NMR,thermal analysis and N2 adsorption-desorption measurements.After soluble ions are removed,the interactors between surfactant micelles and silicate polymers are reorganized and then form mesostructures 1 he hexagonal framework is sonsistent with amorphous silica gel.The structures of materials depend on the synthesis conditions Hydrothermal process improves the interactions between molecules and increases the degree of framework silicon atom polymerization The.surface area and the mesopore volume of the material prepared at 100℃ increase by 87% and 71 %,respectively,compared with those obtained at room temperature.
At low concentrations of cetyltrimethylammonium bromide,all silica-based mesoporous materials with hexagonal phase have been synthesized via interactions between self-assembled surfactant molecule aggregates and aniomc silicate polymers.The resulting materials are characterized by XRD,FT-IR,solid state 29Si MAS NMR,thermal analysis and N2 adsorption-desorption measurements.After soluble ions are removed,the interactors between surfactant micelles and silicate polymers are reorganized and then form mesostructures 1 he hexagonal framework is sonsistent with amorphous silica gel.The structures of materials depend on the synthesis conditions Hydrothermal process improves the interactions between molecules and increases the degree of framework silicon atom polymerization The.surface area and the mesopore volume of the material prepared at 100℃ increase by 87% and 71 %,respectively,compared with those obtained at room temperature.
基金
ProJect supported by the National Natural Science Foundation of China