The strain softening characteristics analysis of 12Cr1MoV streel friction welding pipe joints.which were removed from heating apparatus pipes ager over 9 and is yearly of service, was undertaken. It is concluded that the evident softening did not occur in the weld metal and HAZ during serice. whereas it did in the base metal 2mm apart from the center of the weld metal. The difference is due to the restriction of the pipe hoop, which is formed on the joint during friction welding. The bainite. microstructure in the weld metal and HA Z, which is harder than the pearlite, pecrostpucture in the base metal, makes contpibution too. ThIS phenomenon is peculiar to the friction weldings pipes.
The strain softening characteristics analysis of 12Cr1MoV streel friction welding pipe joints.which were removed from heating apparatus pipes ager over 9 and is yearly of service, was undertaken. It is concluded that the evident softening did not occur in the weld metal and HAZ during serice. whereas it did in the base metal 2mm apart from the center of the weld metal. The difference is due to the restriction of the pipe hoop, which is formed on the joint during friction welding. The bainite. microstructure in the weld metal and HA Z, which is harder than the pearlite, pecrostpucture in the base metal, makes contpibution too. ThIS phenomenon is peculiar to the friction weldings pipes.