Observation of dislocation configurations was conducted for aged and compressive deformed (Ni64A136) FeMoB alloy after hot isostatic pressing (HIP). It isshown that short and straight parallel dislocations are present in the matrix of NiAI alloy.Long and tortuous dislocations and superdislocations appear in the 1%-deformed specimen. As the compressive strain increases to 2. 6%, high-densities dislocations appear inand between the deformation bands. The dislocations become tangled up in the specimencompressed to a strain of 6. 2 %.
Observation of dislocation configurations was conducted for aged and compressive deformed (Ni64A136) FeMoB alloy after hot isostatic pressing (HIP). It isshown that short and straight parallel dislocations are present in the matrix of NiAI alloy.Long and tortuous dislocations and superdislocations appear in the 1%-deformed specimen. As the compressive strain increases to 2. 6%, high-densities dislocations appear inand between the deformation bands. The dislocations become tangled up in the specimencompressed to a strain of 6. 2 %.