摘要
The nitride in 30CrNi steel and its composition along boundaries have been studied by means of scanning Auger microprobe.The nitride identified metallographically is Zr(C,N)which contains a small amount of Ti and O.The interface width between the Zr(C,N)and the matrix is about 1.6 μm.An Fe-rich shell is.found on the surface of Zr(C,N)which appeared on the fracture surface.The thickness of shell is 0.1-0.8μm.The Fe concentration of its outmost layer is 3-18 at.-% and decreases exponentially along the depth direction.
The nitride in 30CrNi steel and its composition along boundaries have been studied by means of scanning Auger microprobe.The nitride identified metallographically is Zr(C,N)which contains a small amount of Ti and O.The interface width between the Zr(C,N)and the matrix is about 1.6 μm.An Fe-rich shell is.found on the surface of Zr(C,N)which appeared on the fracture surface.The thickness of shell is 0.1-0.8μm.The Fe concentration of its outmost layer is 3-18 at.-% and decreases exponentially along the depth direction.