摘要
The PVC/EBBA ultrathin composite membranes with thickness of about 100 nm were prepared by spreading the solution on water surface. The overlapped composite membrane showed a characteristic aggregation structure in which the polymer matrix exists as a three-dimensional spongy network and the liquid crystal domains werc observed. Tne surface modification for the overlapped membranes was carried out by means of plasma-polymerization with the monomers of fluorocarbon compounds. Both Arrhenius plots of permeability coefficients for oxygen ((?)_O_2) in the membrane samples before and after modification showed significant increase in the vicinity of the T_(KN) of EBBA.
The PVC/EBBA ultrathin composite membranes with thickness of about 100 nm were prepared by spreading the solution on water surface. The overlapped composite membrane showed a characteristic aggregation structure in which the polymer matrix exists as a three-dimensional spongy network and the liquid crystal domains werc observed. Tne surface modification for the overlapped membranes was carried out by means of plasma-polymerization with the monomers of fluorocarbon compounds. Both Arrhenius plots of permeability coefficients for oxygen ((?)_O_2) in the membrane samples before and after modification showed significant increase in the vicinity of the T_(KN) of EBBA.
基金
Supported by the Science Fund of Academia Sinica and the National Natural Science Foundation of China