摘要
In order to clarify that the IFP and the “Type 2”α phase are also arising from TiC,a metastable β-Ti alloy was selected for investigation in this work.The results showed that af- ter heating the alloy just below the α+β→β transus temperature and quenching,the TiC lay- er existed at the α/β interface.The morphology of TiC is similar to that of the IFP arising from TiH_2 in the α-β two-phase alloys.The IFP TiC also provided an easy crack path or the crack initiation sites.The fracture is also identical to that caused by IFP TiH_2.The arced diffractions(characteristic of “Type 2”α)were found in the selected area diffraction pat- terns of some specimens which had been isothermally aged after solid solution treatment.The particles which bring on the arced diffractions may be TiC on the basis of structure and lat- tice parameter analysis,not the so called “Type 2”α phase.
In order to clarify that the IFP and the “Type 2”α phase are also arising from TiC,a metastable β-Ti alloy was selected for investigation in this work.The results showed that af- ter heating the alloy just below the α+β→β transus temperature and quenching,the TiC lay- er existed at the α/β interface.The morphology of TiC is similar to that of the IFP arising from TiH_2 in the α-β two-phase alloys.The IFP TiC also provided an easy crack path or the crack initiation sites.The fracture is also identical to that caused by IFP TiH_2.The arced diffractions(characteristic of “Type 2”α)were found in the selected area diffraction pat- terns of some specimens which had been isothermally aged after solid solution treatment.The particles which bring on the arced diffractions may be TiC on the basis of structure and lat- tice parameter analysis,not the so called “Type 2”α phase.
作者
YU Xuejie WANG Jianlin Shanghai Iron and Steel Research Institute,Shanghai,ChinaZHOU Tianjian Anhui Institute of Technology,Hefei,China YU Xuejie,Senior Engineer,Shanghai Iron Steel Research Institute,1001 Taihe Road,Wusong,Shanghai,China.