摘要
The phase boundary,of α_2 precipitation at 600℃ in Ti-AI-La ternary system has been de- termined by TEM examination,which shows three kinds of phase regions,namely the single α phase region,the transitional phase region where there is superlattice reflection but no α_2 precipitation,and the α+α_2 region.A point of maximum aluminium content was found to exist on the α/(α+α_2)boundary and the track of the boundary was explained in terms of the internal oxidation of lanthanum and the electron concentration rule for α_2 formation.
The phase boundary,of α_2 precipitation at 600℃ in Ti-AI-La ternary system has been de- termined by TEM examination,which shows three kinds of phase regions,namely the single α phase region,the transitional phase region where there is superlattice reflection but no α_2 precipitation,and the α+α_2 region.A point of maximum aluminium content was found to exist on the α/(α+α_2)boundary and the track of the boundary was explained in terms of the internal oxidation of lanthanum and the electron concentration rule for α_2 formation.