摘要
The melting behavior,solid state phase transformation and structure of pseudo-ternary compounds Nd_2(Fe_(1-x)Ni_x)_(14)B and Pr_2(Co_(1-y)Ni_y)_(14)B were studied using differential thermal analysis,optical microscopy X-ray diffraction,and electron probe micro-analysis techniques.At high temperature,eutectoid decomposition R_2(Ni,M)_(17)→R(Ni,M)_5+x-Ni(M) takes place in these two pseudo-ternary compounds,in the composition range x=0.6～1.0 and y=0.3～1.0,respectively.When x(or y)≤0.2,both Nd_2(Fe_(1-x)Ni_x)_(14)B and Pr_2(Co_(1-y)Ni_y)_(14)B are single phase tetragonal.The phase constitutents of these two systems at room tempera- ture are similar in the composition range 0.6≤x(or y)≤1.0.
The melting behavior,solid state phase transformation and structure of pseudo-ternary compounds Nd_2(Fe_(1-x)Ni_x)_(14)B and Pr_2(Co_(1-y)Ni_y)_(14)B were studied using differential thermal analysis,optical microscopy X-ray diffraction,and electron probe micro-analysis techniques.At high temperature,eutectoid decomposition R_2(Ni,M)_(17)→R(Ni,M)_5+x-Ni(M) takes place in these two pseudo-ternary compounds,in the composition range x=0.6～1.0 and y=0.3～1.0,respectively.When x(or y)≤0.2,both Nd_2(Fe_(1-x)Ni_x)_(14)B and Pr_2(Co_(1-y)Ni_y)_(14)B are single phase tetragonal.The phase constitutents of these two systems at room tempera- ture are similar in the composition range 0.6≤x(or y)≤1.0.
基金
the National Natural Science Fundation of China.