The effect of barnacles on corrosion of low alloy (16Mn) steel was studied by immersing steel panels in seawater at Zhonggang.Qingdao, for 41 months. It was found that the secondary attachment on this kind of steel by barnacles had less effect on its corrosion while the primary attachment had a greater effect; that different seasons have different effects on the form and extent of local corrosion in this steel, and that primarily attached barnacles cause more serious local corrosion in high breeding seasons when there are more attachments.
The effect of barnacles on corrosion of low alloy (16Mn) steel was studied by immersing steel panels in seawater at Zhonggang.Qingdao, for 41 months. It was found that the secondary attachment on this kind of steel by barnacles had less effect on its corrosion while the primary attachment had a greater effect; that different seasons have different effects on the form and extent of local corrosion in this steel, and that primarily attached barnacles cause more serious local corrosion in high breeding seasons when there are more attachments.