The effect of temperature and chloride ion concentration on the electrochemical behaviour of austenitic-ferritic duplex stainless steel COR 25 in an aqueous solution of 60%H_3PO_4+4%H_2SO_4 is studied in this paper. The experiments show that the anodic active peak current on potentiodynamic polarization increases by an order of magnitude with an in- crease of temperature from 50℃ and with an increase of chloride ion from<1 mg/1 to 1500mg/1. Compared with the other materials tested, the austenitic-ferritic duplex stainless steel shows favourable corrosion characteristics in electrochemical tests,being comparable to the fully austenitic alloy Sanicro 28,which has a higher chromium and nickel content,and is much better than GX3CrNiMo2010.Corrosion of the duplex material is normally phase selec- tive,with phase boundary attack after unfavour- able heat treatments.
The effect of temperature and chloride ion concentration on the electrochemical behaviour of austenitic-ferritic duplex stainless steel COR 25 in an aqueous solution of 60%H_3PO_4+4%H_2SO_4 is studied in this paper. The experiments show that the anodic active peak current on potentiodynamic polarization increases by an order of magnitude with an in- crease of temperature from 50℃ and with an increase of chloride ion from<1 mg/1 to 1500mg/1. Compared with the other materials tested, the austenitic-ferritic duplex stainless steel shows favourable corrosion characteristics in electrochemical tests,being comparable to the fully austenitic alloy Sanicro 28,which has a higher chromium and nickel content,and is much better than GX3CrNiMo2010.Corrosion of the duplex material is normally phase selec- tive,with phase boundary attack after unfavour- able heat treatments.