上压渗流铸造法制备泡沫铝 被引量:2

Preparation of Foamed Aluminum by Means of Penetrating Casting
下载PDF
导出
摘要 采用上压渗流铸造法,利用盐粒和陶瓷网作为预制体,制备了开孔泡沫铝和闭孔泡沫铝,并对其孔隙率、透气性和显微硬度等性能进行了测试、分析.研究结果表明,上压渗流铸造法可制备出孔隙率高、透气性好的泡沫铝,且开孔泡沫铝的孔隙率都大于闭孔泡沫铝,而闭孔泡沫铝的硬度高于开孔泡沫铝.通过分析制备工艺参数发现,模具和预制体的预热温度在400~500℃、浇注温度在750—780℃、充型压力不超过0.5MPa时,可制备出性能良好、结构完整的泡沫铝. Foam aluminums with open pores and closed pores are prepared using the preforms in form of the salt grain and ceramic mesh, respectively, by means of penetrating casting technology. Some of properties of the foam aluminums, such as porosity, permeability and micro-hardness, are tested and analyzed. The results show that the foam aluminums have high porosity and excellent permeability by means of penetrating casting technology. The porosities of the foam aluminums with open pores are larger than that of the foam aluminums with closed pores. And the micro-hardness of the foam aluminums with closed pores is higher than that of the foam aluminums with open pores. Through the analysis of preparation process parameters, it is found that the preheating temperatures of the salt grains, ceramic mesh and mold should be in the range of 400-500℃, the pouring temperature in the range of 750 - 780℃ and the filling mold pressure not more 0.5 MPa.
出处 《沈阳理工大学学报》 CAS 2009年第1期18-21,25,共5页 Journal of Shenyang Ligong University
关键词 泡沫铝 渗流铸造 孔隙率 工艺参数 foam aluminum penetrating casting porosity process parameters
  • 相关文献

参考文献10

二级参考文献60

共引文献95

同被引文献13

引证文献2

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部