La_(2/3)Sr_(1/3)MnO_3/ZnO混合物薄膜的磁电阻和伏安特性研究 被引量:3

Magnetroresistance and Current-voltage Characteristics in La_(2/3)Sr_(1/3)MnO_3/ZnO Composite Films
下载PDF
导出
摘要 利用脉冲激光沉积的方法在Si(100)氧化成SiO2的基片上制备了(La2/3Sr1/3MnO3)x/(ZnO)1-x混合物薄膜,研究了薄膜的磁电阻和伏安特性.X射线衍射分析表明,除了衬底SiO2的衍射峰以外,分别出现了La2/3Sr1/3MnO3(101)的衍射峰和ZnO(002)的衍射峰,且它们形成了两相共存体系.实验表明:x=0.3的混合物薄膜表现为半导体导电特性,而x=0.4的样品则出现了典型的金属-绝缘相变.所制备的样品表现出了低场磁电阻效应和非线性伏安特性.在0.7T磁场的作用下,x=0.3的样品在温度为60K时取得的最大磁电阻值为28.8%.通过对伏安关系拟合表明,在La2/3Sr1/3MnO3和ZnO颗粒之间存在一定的耗尽层,且产生了界面缺陷态. Magnetroresistance and current-voltage characteristics of the composite (La2/3 Sr1/3 MnO3 )x/ (ZnO) 1-x films prepared by the pulsed laser deposition method on Si(100) suhstrates oxidized by SiO2 were investigated. XRD patterns indicate that ZnO and LSMO have (002) and (101) dominant orientations, respectively, and they form the coexisting system of two phases. Experimental results show the film with x = 0.3 favors a semieonductive conduction and the film with x = 0.4 exhibits the typical insulator-metal (I-M) transition. The films have the low field magnetoresistance(LFMR) effect and the nonlinear currentvoltage characteristics. The maximum LFMR value of the film with x = 0.3 is about 28.8% at T = 60K under an applied magnetic field of about 0.7T. The current-voltage fitting shows that a great number of interface states appear at the depletion between La2/3Sr1/3 MnO3and ZnO grains due to the mismatch of the lattice.
出处 《无机材料学报》 SCIE EI CAS CSCD 北大核心 2009年第3期591-594,共4页 Journal of Inorganic Materials
基金 国家自然科学基金(50331040 50702046) 西北工业大学翱翔之星项目
关键词 锰氧化物颗粒薄膜 磁电阻效应 伏安特性 manganites composite film magnetoresistance current-voltage characteristics
  • 相关文献

参考文献25

  • 1Jin S,Tuefel T H,Fastnacht R A,et al.Science,1994,264(5157):413-417.
  • 2赵省贵,陈长乐,金克新.Pr2/3Sr1/3MnO3薄膜外场诱导自旋输运特性[J].无机材料学报,2008,23(2):281-285. 被引量:1
  • 3Jin K X,Chen C L,Wang S L,et al.J.Appl.Phys.,2004,96(3):1537-1539.
  • 4Milner A,Gerber A,Grolsman B,et al.Phys.Rev.Lett.,1996,76(3):475-478.
  • 5Coey J M D,Berkowlt A E,Barcells L,et al.Phys.Rev.Lett.,1998,80(17):3815-3818.
  • 6Hwang J Y,Cheong S W.Science,1997,278(5343):1607-1609.
  • 7刘俊明,王克锋.稀土掺杂锰氧化物庞磁电阻效应[J].物理学进展,2005,25(1):82-130. 被引量:46
  • 8Xiao Q J,Jiang J S,Chien C L.Phys.Rev.Lett.,1992,68(25):3749-3752.
  • 9Berkowitz A E,Mitchell J R,Carey M J,et al.Phys.Rev.Lett.,1992,68(25):3745-3748.
  • 10Gieny B,Chamberod A,Genin J B,et al.J.Magn.Magn.Mater.,1993,126(1-3):433-436.

二级参考文献190

共引文献95

同被引文献28

引证文献3

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部