摘要
针对某产品中部分30MnNiMoCuBRe铸钢件的断口中存在的杆状结晶组织缺陷,设计了多套热处理工艺方案进行试验对比不同工艺条件下的宏观断口、微观晶粒度和力学性能,找到纠正该缺陷的一种热处理工艺方法。
In order to solve problem of as-east defects in 30MnHiMoCuBRe,this paper designs a series of fabrication processing scheme to make experiment,discovers a heat treatmene proeess to correct the defects with eomparation of maer fraeture,mirro grain size and mechanical property in different situation.
出处
《机械管理开发》
2009年第3期90-91,共2页
Mechanical Management and Development
关键词
杆状结晶
均匀化热处理
缺陷
Bar crystallization
Homogenizing heat treatment
Defects