烧结法制备氧化锆-氧化铝复合微滤膜 被引量:6

Preparation of zirconia-alumina composite microfiltration membrane by sintering
下载PDF
导出
摘要 采用悬浮粒子烧结法,在两种不同结构的α-Al2O3支撑体上制备出017μm左右的管式氧化锆复合微滤膜研究制膜条件对ZrO2/α-Al2O3复合微滤膜的成膜质量的影响,结果发现,要得到无缺陷膜,干燥和烧结的温度及时间的适当控制尤为重要,温度为bTs烧结2h成膜较好采用气体泡压法测定膜的孔径分布。 The composite tubular membranes are prepared by applying suspensions of zirconia particles to form separation layers on two different porous α-alumina supports and heating the coated supports to partly sinter the particles of the layers.The conditions of making the zirconia composite membranes are investigated systematically.It is very important for the crack-free composite membranes to control temperature and time of drying and sinterin.The pore size distributions of the asymmetric zirconia membranes are determined by gas bubble pressure method.The water permeabilities of these membranes are also measured.
出处 《膜科学与技术》 CAS CSCD 1998年第1期18-21,30,共5页 Membrane Science and Technology
关键词 氧化锆 复合微滤膜 粒子烧结 氧化铝 膜分离 zirconia\ composite microfiltration membrane\ particles sintering\ preparation\ charaterization
  • 相关文献

参考文献7

  • 1黄培,邢卫红,徐南平,时钧.气体泡压法测定无机微滤膜孔径分布研究[J].水处理技术,1996,22(2):80-84. 被引量:36
  • 2王零森,特种陶瓷,1996年
  • 3黄培,博士学位论文,1996年
  • 4时钧,化工进展,1995年,1期,45页
  • 5徐南平,化工进展,1995年,3期,7页
  • 6王沛,第七届全国化工年会论文集,1994年,592页
  • 7李世普,特种陶瓷工艺学,1991年,99页

共引文献35

同被引文献38

引证文献6

二级引证文献41

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部