A single layer of CoFeB and a multilayer of CoFeB MgO films are prepared by means of DC/RF magnetron sputter deposition. The excellent microwave properties and high electrical resistivity are simultaneously achieved in the discontinuous multilayer structure of [Co44Fe44B12（0.7nm）/MgO（0.4nm）]40 film. This film has a high permeability （μ′） （larger than 100 below 2.1 GHz）, a high magnetic loss （μ″） （larger than 100 in a range from 1.5 to 3.3GHz）, a resistivity of 3.3 × 10^3μΩ. cm, a saturation magnetization of 1.2 T, and an in-plane uniaxial anisotropy field of 5.5 kA/m. The microstructure and the surface topography of the film are also analysed. The relatively large surface roughness for the discontinuous film is responsible for the wide frequency band of magnetic loss. The magnetic loss and the high resistivity indicate that the discontinuous CoFeB MgO multilayer film has potential applications in microwave absorbers and electromagnetic interference （EMI） shielding materials in a GHz frequency range.
A single layer of CoFeB and a multilayer of CoFeB MgO films are prepared by means of DC/RF magnetron sputter deposition. The excellent microwave properties and high electrical resistivity are simultaneously achieved in the discontinuous multilayer structure of [Co44Fe44B12（0.7nm）/MgO（0.4nm）]40 film. This film has a high permeability （μ′） （larger than 100 below 2.1 GHz）, a high magnetic loss （μ″） （larger than 100 in a range from 1.5 to 3.3GHz）, a resistivity of 3.3 × 10^3μΩ. cm, a saturation magnetization of 1.2 T, and an in-plane uniaxial anisotropy field of 5.5 kA/m. The microstructure and the surface topography of the film are also analysed. The relatively large surface roughness for the discontinuous film is responsible for the wide frequency band of magnetic loss. The magnetic loss and the high resistivity indicate that the discontinuous CoFeB MgO multilayer film has potential applications in microwave absorbers and electromagnetic interference （EMI） shielding materials in a GHz frequency range.
基金
supported by the National Natural Science Foundation of China(Grant Nos 50371029 and 50771047)
the Program for the New Century Excellent Talents in University of the Ministry of Education,China(Grant No NCET20420702)
the Natural Science Foundation for the Distinguished Scholars of Hubei Province,China(Grant No 2005ABB002)