摘要
以硅酸钠和盐酸为原料,用化学沉淀法制备高比表面多孔SiO2,并对其性能进行了研究.结果表明,所合成的SiO2比表面积可达1300m2/g以上,具有蜂窝状的微孔,孔径均匀,而且性能稳定.
The synthesis and characterization of the amorphous porous silica are reported in this paper. The silica was prepared by chemical precipitation from sodium silicate and chlorohydric acid in the presence of a surfactant, and the silica powders with a high specific surface area ( >1 300 m 2/g) has a uniform pore diamater about 2 7 nm.