摘要
Effects of different heat treatment temperatures on properties of Chinese calcined flint clay based plastic refractories were investigated using Chinese calcined flint clay as starting material, aluminum sulfate and fireclay as binding system. The results showed that with temperature rising, Chinese calcined flint clay based plastic refractories shrinked firstly and then expanded. The modulus of rupture （MOR） and the cold crushing strength （CCS） inereased firstly and then decreased from 110 ℃ to 600 ℃ , then increased obviously. Thermal expansion coefficient increased from 110 ℃ to 760 ℃, decreased from 760 ℃ to 1 300 ℃ , and increased from 1 300 ℃ to1500 ℃.
Effects of different heat treatment temperatures on properties of Chinese calcined flint clay based plastic refractories were investigated using Chinese calcined flint clay as starting material, aluminum sulfate and fireclay as binding system. The results showed that with temperature rising, Chinese calcined flint clay based plastic refractories shrinked firstly and then expanded. The modulus of rupture （MOR） and the cold crushing strength （CCS） inereased firstly and then decreased from 110 ℃ to 600 ℃ , then increased obviously. Thermal expansion coefficient increased from 110 ℃ to 760 ℃, decreased from 760 ℃ to 1 300 ℃ , and increased from 1 300 ℃ to1500 ℃.