负载Ni炭气凝胶的制备及结构性能研究 被引量:1

Preparation and study of structure,property of nickel-dispersed activated carbon aerogels
下载PDF
导出
摘要 以间苯二酚、甲醛为原料,添加适量的十二烷基苯磺酸钠,再加入不同浓度的乙酸镍溶液,在85℃水浴中聚合;经溶胶-凝胶、溶剂置换、常压干燥和1000℃氮气气氛下热解,得到负载不同含量金属Ni的炭气凝胶。利用透射电镜(TEM)、扫描电境(SEM)、X射线衍射(XRD)、比表面积及孔径分析(BET)和直流充放电测试等手段,对比讨论了负载不同含量金属Ni对炭气凝胶的结构和性能的影响。结果表明,这种方法可以均匀地将Ni纳米粒子分散于炭气凝胶中;适量的金属Ni可使炭气凝胶的比表面积及充放电性能得到显著提高;如负载Ni含量过高则炭气凝胶石墨化程度增加。 Nickel-dispersed carbon aerogels have been prepared using dodecylbenzene sulfonic acid sodium salt and nickel acetate of different concentrations as catalyst based upon a polycondensation of resorcinol with formaldehyde at 85℃ and an ambient pressure drying followed by carbonization at 1000℃. Resulting carbon aerogels (CAs) have been investigated in detail by TEM,SEM, XRD, BET and charge-discharge current test. Discuss the effect of different content of nickel to structure and property of CAs. It was found that nickel particles was dispersed regularly in CAs; the appropriate amount of nickel could increase the specific surface area and specific capacitance evidently, more nickel made CAs tend to graphite.
出处 《功能材料》 EI CAS CSCD 北大核心 2009年第6期949-952,共4页 Journal of Functional Materials
基金 国家自然科学基金资助项目(50502004) 北京市科技新星计划资助项目(2007B020)
关键词 炭气凝胶 常压干燥 负载金属Ni 电化学性能 carbon aerogels subcritical nickel-dispersed
  • 相关文献

参考文献1

  • 1T.H. Zhang, Z.Z. Yi, X. Y. Wu, S.J. Zhang, Y. G. Wu, X. Zhang, H.X. Zhang, A.D. Liu and X.J. Zhang Key Laboratory for Radiation Beam Technology and Material Modification, Institute of Low Energy Nuclear Physics, Beijing Normal University, Beijing Radiatio.Mo SILTCIDE SYNTHISIS BY DUAL ION BEAM DEPOSITION[J].Acta Metallurgica Sinica(English Letters),2002,15(2):187-190. 被引量:76

二级参考文献7

  • 1[6]T.H. Zhang and Y.G. Wu, Nuclear Technology 18 (1995) 577.
  • 2[7]T.H. Zhang and Y.G. Wu, J. Beijing Normal University (Natural Science) 30 (1994) 479.
  • 3[1]S.S. L au, J.S.-Y. Feng, J.O. Olowolafe and M.-A. Nicolet, Mayer, Thin Solid Film 25 (1975) 415.
  • 4[2]S. Mantl, Material Science Report 8 (1992) 1.
  • 5[3]T.H. Zhang, J. Chen, G.R. Sun, Y.G. Wu, Y. Luo and X.J. Ding, Surface and Coating Technology 66(1994) 355.
  • 6[4]T.H. Zhang, Y.G. Wu, H. Liang, W.D. Qian and Y. Luo, J. Beijing Normal University (Natural Science)30 (1994) 357.
  • 7[5]T.H. Zhang and Y.G. Wu, Chinese Journal of Semiconductors 21(6) (2000) 542.

共引文献75

同被引文献15

  • 1余刚,杨志华,祝万鹏,蒋展鹏.染料废水物理化学脱色技术的现状与进展[J].环境科学,1994,15(4):75-79. 被引量:90
  • 2Guifen Lv, Dingcai Wu, Ruowen Fu. Performance of carbon acrogels particle electrodes for the aqueous phase electro-catalytic oxidation of simulated phenol wastewaters. J. Hazard. Mater., 2009, 165(3):961-966.
  • 3Polcaro A. M. , Palmas S. , Renoldi F. , et al. Three-dimensional electrodes for the electrochemical combustion of organic pollutants. Electrochim. Acta, 2000, 46 ( 3 ) : 389-394.
  • 4Neti Nageswara Rao, Misra Rohit, Gedam Nitin, et al. Kinetics of electrooxidation of landfill leaehate in a three-dimensional carbon bed electrochemical reactor. Chemosphere, 2009, 76(9) :1206-1212.
  • 5Minghua Zhou, Wei Wang, Meiling Chi. Enhancement on the simultaneous removal of nitrate and organic pollutants from groundwater by a three-dimensional bio-electrochemical reactor. Bioresour. Technol. , 2009, 100 (20) :4662- 4668.
  • 6Pekala R, W. Organic aerogels from the polycondensation of resorcinol with formaldehyde. J. Mater. Sci. , 1989, 24(10) :3221-3227.
  • 7Sanroman M. A. , Pazos M. , Ricart M. T. , et al, Electrochemical decolourisation of structurally different dyes. Chemosphere, 2004, 57 (3) :233-239.
  • 8Fernandes A. , Morro A. , Magrinho M. , et al. Electrochemical degradation of C. I. Acid Orange 7. Dyes and Pigments, 2004, 61 (3):287-296.
  • 9Goncalves M. , Joyee A. , Alves M. , et al. Anodic oxidation of oleate for wastewater treatment. Desalination, 2005, 185(3) :351-355.
  • 10Hongzhu Ma, Bo Wang, Xiaoyan Luo. Studies on degradation of methyl orange wastewater by combined electrochemical process. Journal of Hazardous Materials, 2007, 149(2):492-498.

引证文献1

二级引证文献7

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部