摘要
Electrochemical, thermal, and photophysical properties of novel two- （BPODPA）, four- （BBPOPA）, and six-branch （TBPOA） triphenylamine chromophores are studied. The decomposition temperature of chro- mophores reaches 373 - 412 ℃. The electrochemical properties is explored by cyclic voltammetry. The ionization potential of chromophores is in the range of 5.14 - 5.18 eV. Excitation at 400 nm reveals emission peaks at 483 - 487 nm and the fluorescence quantum yields are 0.73 - 0.75 in CH2Cl2. Two-photon absorption （TPA） properties of chromophores are measured by nonlinear transmission method. The maximum TPA cross-section values are measured at 758 nm to be 20369 GM （1 GM=10^-50 cm^4 -s/photon） for TBPOA, 7024 GM for BBPOPA, and 1227 GM for BPODPA, respectively. When pumped with 800-nm laser irradiation, chromophores show strong two-photon excited blue-green fluorescence at 502 - 518 nm. These results provide a basis for understanding the electronic and optical properties of the conjugated multi-branch chromoohore in terms of the underlying molecular and electronic structures.
Electrochemical, thermal, and photophysical properties of novel two- （BPODPA）, four- （BBPOPA）, and six-branch （TBPOA） triphenylamine chromophores are studied. The decomposition temperature of chro- mophores reaches 373 - 412 ℃. The electrochemical properties is explored by cyclic voltammetry. The ionization potential of chromophores is in the range of 5.14 - 5.18 eV. Excitation at 400 nm reveals emission peaks at 483 - 487 nm and the fluorescence quantum yields are 0.73 - 0.75 in CH2Cl2. Two-photon absorption （TPA） properties of chromophores are measured by nonlinear transmission method. The maximum TPA cross-section values are measured at 758 nm to be 20369 GM （1 GM=10^-50 cm^4 -s/photon） for TBPOA, 7024 GM for BBPOPA, and 1227 GM for BPODPA, respectively. When pumped with 800-nm laser irradiation, chromophores show strong two-photon excited blue-green fluorescence at 502 - 518 nm. These results provide a basis for understanding the electronic and optical properties of the conjugated multi-branch chromoohore in terms of the underlying molecular and electronic structures.
基金
supported by the National Natural Science Foundation of China (Nos.60678042 and 60708024)
the Natural Science Foundation of Jiangsu Province of China (No.BK2006553)
the Natural Science Foundation of Southeast University (No.9207041399)